Description
Chinese Refractory raw material resources are abundant, which are suitable for the production of various grades of insulating firebrick. Limiting temperature of use range from 900¡æ to 1650¡æ.Each grade of insulating firebrick is formulated to meet specific thermal and physical requirements.
Top grade insulating firebrick are made from high-purity refractory clays, with graduated additions of alumina for the higher temperature products, and a carefully graded organic filler, which burns out during manufacture to give a controlled, uniform lacuna structure. Each brick machined to precise size on all six faces. The maximum continue use temperature depends on application.
Features
1. Low thermal conductivity
2. Low thermal capacitance
3. Low impurity content
4. High hot compressive strength
5. Accurate dimension
Typical application
Recommended for use as a primary hot face refractory lining or as back-up insulation behind other refractory in furnace, kilns, flues, refining vessels, heaters, regenerators, gas producers and main, soaking pits, annealing furnace, catalyst case and similar high temperature industrial equipment.
specification
Items
|
Testing Temperature(¡æ)
When reheated with 2% contracting rate |
Volume Density
g/cm3 |
Pressure Strength
Mpa |
Thermal Conductivity
kcal/mh¡æ
(350¡æ) |
A |
A-1 |
900 |
¡Ü0.50 |
¡Ý0.50 |
¡Ü0.13 |
A-2 |
1000 |
¡Ü0.50 |
¡Ý0.50 |
¡Ü0.14 |
A-3 |
1100 |
¡Ü0.50 |
¡Ý0.50 |
¡Ü0.15 |
A-4 |
1200 |
¡Ü0.55 |
¡Ý0.80 |
¡Ü0.16 |
A-5 |
1300 |
¡Ü0.60 |
¡Ý0.80 |
¡Ü0.17 |
A-6 |
1400 |
¡Ü0.70 |
¡Ý1.00 |
¡Ü0.20 |
A-7 |
1500 |
¡Ü0.75 |
¡Ý1.00 |
¡Ü0.22 |
B |
B-1 |
900 |
¡Ü0.70 |
¡Ý2.50 |
¡Ü0.17 |
B-2 |
1000 |
¡Ü0.70 |
¡Ý2.50 |
¡Ü0.18 |
B-3 |
1100 |
¡Ü0.75 |
¡Ý2.50 |
¡Ü0.20 |
B-4 |
1200 |
¡Ü0.80 |
¡Ý2.50 |
¡Ü0.22 |
B-5 |
1300 |
¡Ü0.80 |
¡Ý2.50 |
¡Ü0.23 |
B-6 |
1400 |
¡Ü0.90 |
¡Ý3.00 |
¡Ü0.27 |
B-7 |
1500 |
¡Ü1.00 |
¡Ý3.00 |
¡Ü0.31 |
C |
C-1 |
1300 |
¡Ü1.10 |
¡Ý5.00 |
¡Ü0.30 |
C-2 |
1400 |
¡Ü1.20 |
¡Ý7.00 |
¡Ü0.38 |
C-3 |
1500 |
¡Ü1.25 |
¡Ý10.00 |
¡Ü0.45 |
Main property
|
Classify
temperature
¡æ |
Apparent density
kg/m3 |
Chemical component Wgt % |
Bending strength
Mpa |
Cold crushing strength
Mpa |
Al2 O3
% |
SiO2
% |
Fe2 O3
% |
K2 O + Na2O
% |
DM20 |
1100 |
550 |
45.00 |
50.00 |
1.00 |
1.00 |
0.70 |
0.80 |
DM23 |
1260 |
530 |
45.00 |
51.00 |
0.80 |
0.72 |
0.70 |
1.00 |
DM25 |
1350 |
800 |
52.00 |
41.55 |
0.62 |
0.81 |
1.20 |
1.80 |
DM26 |
1430 |
780 |
59.00 |
37.00 |
0.70 |
0.70 |
1.80 |
2.00 |
DM28 |
1540 |
880 |
64.00 |
32.00 |
0.60 |
0.60 |
2.00 |
2.50 |
DM30 |
1600 |
1000 |
70.00 |
28.00 |
0.33 |
0.21 |
2.00 |
3.00 |
JM23 |
1260 |
480 |
37.00 |
44.40 |
0.70 |
1.10 |
1.00 |
1.20 |
JM26 |
1430 |
800 |
58.00 |
39.10 |
0.70 |
1.70 |
1.50 |
1.60 |
JM28 |
1540 |
890 |
67.10 |
31.00 |
0.60 |
0.90 |
1.80 |
2.10 |
JM30 |
1650 |
1020 |
73.40 |
25.10 |
0.50 |
0.90 |
2.10 |
2.20 |
|